PA 66 / 6 Glass-fiber Reinforced Grade
Introduction
This product is a composite of PA 66 / 6 and 15%, 30% or 45% glass-fiber. There are natural and black colors. Natural color granule could be dyed in various colors. It has excellent stiffness, dimensional stability, heat-resistance and surface appearance. It is suitable for producing articles demanding good appearances and requiring decoration process parts.
Applications
1. Accessories of the camera
2. Handles of the car door
3. Fasteners
4. Legs of the chair
5. Cover of the knife
2. Handles of the car door
3. Fasteners
4. Legs of the chair
5. Cover of the knife
Features
1. Good stiffness
2. Thermal-resistance
3. Good surface appearance
4. Easy to be painted / coated
2. Thermal-resistance
3. Good surface appearance
4. Easy to be painted / coated
Mechanical properties | Standard | Unit | Test sample conditions | PA 66 / 6 Glass-fiber Reinforced Grade | ||
---|---|---|---|---|---|---|
G-4215 | G-4233 | G-4245 | ||||
Tensile Strength at Yield | ASTM D638 | Kg/cm2 | Dry / Cond* | 1250 / 750 | 1500 / 1350 | 2210 / 1600 |
Elongation at Break | ASTM D638 | % | Dry / Cond* | 4 / 17 | 7 / 11 | 4 / 7 |
Tensile Strength at Break | ASTM D638 | Kg/cm2 | Dry / Cond* | 960 / 520 | 1600 / 1350 | 1500 / 1050 |
Tensile modulus | ASTM D638 | Kg/cm2 | Dry / Cond* | 48000 / 29000 | 61500 / 34700 | 82000 / 62000 |
Flexural strength | ASTM D790 | Kg/cm2 | Dry / Cond* | 1900 / 1000 | 2590 / 2150 | 3300 / 2350 |
Flexural modulus | ASTM D790 | Kg/cm2 | Dry / Cond* | 48870 / 20400 | 61500 / 37000 | 116200 / 66150 |
Izod notched impact strength | ASTM D256 | Kg-cm/cm | Dry / Cond* | 6.5 / 14.0 | 11.5 / 16.5 | 17.5 / 23.0 |
Thermal-fr properties | ||||||
Melting temperature | ASTM E967-DSC | °C | - | 255 | 255 | 255 |
Heat deflection temperature, 4.6 ㎏/cm2 (66 psi) | ASTM D648 | °C | - | - | - | - |
Heat deflection temperature, 18.5 ㎏/cm2 (264 psi) | ASTM D648 | °C | - | 210 | 226 | 220 |
Flammability | UL94 | - | - | HB | HB | HB |
Physical properties | ||||||
Hardness | ASTM D2240 Shore D | D | Dry / Cond* | 80 / 73 | 82 / 80 | 83 / 80 |
Density | ASTM D792 | g/cm3 | - | 1.23 | 1.37 | 1.51 |
Molding shrinkage normal or perpendicular | ASTM D955 | % | - | 0.65 | 0.45 | 0.35 |
Test sample conditions, Test sample conditions, Dry= Measurements at 23°C, RH50. Test after molded 1 - 2 hr. Cond*=Test according to ISO 1110 conditions. For reference only.