PA 6 Impact Modified Grade.
Introduction
This product is a composite of PA 6 and admixtures for enhancing its toughness and impact resistance at low temperature. There are natural and black colors. Natural color granule could be dyed in various colors. The said admixtures are added to improve the sensitivity to impact strength and the strength of thickness of pure PA 6 and to enhance Izod notched impact strength at both room and low temperature.
Applications
1. Water-pot shelf to the bicycle
2. Accessories of the luggage
3. Frame accessories of the stroller
4. Chassis of the skating shoes
5. Handles of the bicycle
6. Accessories of the toy
Features
1. Excellent impact strength at room and low temperature ( -40 ˚ C)
2. Good toughness
3. High flowability
Mechanical properties Standard Unit Test sample conditions PA 6 Impact Modified Grade.
P-4015 P-4020 P-4030
Tensile Strength at Yield ASTM D638 Kg/cm2 Dry / Cond* 490 / 400 480 / 440 455 / 380
Elongation at Break ASTM D638 % Dry / Cond* 80 / 290 135 / 275 270 / 280
Tensile Strength at Break ASTM D638 Kg/cm2 Dry / Cond* 370 / 300 400 / 230 300 / 200
Tensile modulus ASTM D638 Kg/cm2 Dry / Cond* 24000 / 16700 17900 / 16300 16900 / 14300
Flexural strength ASTM D790 Kg/cm2 Dry / Cond* 800 / 350 670 / 260 480 / 180
Flexural modulus ASTM D790 Kg/cm2 Dry / Cond* 18000 / 6300 13580 / 4450 12350 / 3350
Izod notched impact strength ASTM D256 Kg-cm/cm Dry / Cond* 80 / 100 100 / 115 105 / 110
Thermal-fr properties
Melting temperature ASTM E967-DSC °C - 220 220 220
Heat deflection temperature, 4.6 ㎏/cm2 (66 psi) ASTM D648 °C - 120 120 115
Heat deflection temperature, 18.5 ㎏/cm2 (264 psi) ASTM D648 °C - 60 60 60
Flammability UL94 - - HB HB HB
Physical properties
Hardness ASTM D2240 Shore D D Dry / Cond* 74 / 69 65 / 62 64 / 57
Density ASTM D792 g/cm3 - 1.06 1.06 1.03
Molding shrinkage normal or perpendicular ASTM D955 % - 2.10 2.10 2.20
Test sample conditions, Test sample conditions, Dry= Measurements at 23°C, RH50. Test after molded 1 - 2 hr. Cond*=Test according to ISO 1110 conditions. For reference only.
PA 6 Impact Modified / Glass-fiber Reinforced Grade.
Introduction
This product is a composite of PA 6, admixtures for enhancing its toughness and impact resistance at low temperature and 15% or 30% glass-fiber. There are natural and black colors. Natural color granule could be dyed in various colors. The said admixtures are added to improve the sensitivity to impact strength and the strength of thickness of pure PA 6 and to enhance Izod notched impact strength at both room and low temperature. The glass-fiber is added to increase strength, stiffness, dimensional stability and heat-proof property of the substrate. This product is suitable for articles demanding both toughness and stiffness.
Applications
1. Chassis of the skating shoes
2. Accessories of the luggage
3. Sole of sleigh shoes
4. Seat of the golf bag
5. Baby stroller
Features
1. Excellent impact strength at room and low temperature ( -40 ˚ C)
2. Good stiffness
Mechanical properties Standard Unit Test sample conditions PA 6 Impact Modified / Glass-fiber Reinforced Grade.
PG-4015 PG-4030
Tensile Strength at Yield ASTM D638 Kg/cm2 Dry / Cond* 750 / 550 900 / 650
Elongation at Break ASTM D638 % Dry / Cond* 8 / 23 7 / 15
Tensile Strength at Break ASTM D638 Kg/cm2 Dry / Cond* 750 / 550 900 / 650
Tensile modulus ASTM D638 Kg/cm2 Dry / Cond* 28000 / 12900 38500 / 24800
Flexural strength ASTM D790 Kg/cm2 Dry / Cond* 1250 / 850 1400 / 1050
Flexural modulus ASTM D790 Kg/cm2 Dry / Cond* 31000 / 14800 43000 / 22000
Izod notched impact strength ASTM D256 Kg-cm/cm Dry / Cond* 21 / 24 25 / 27
Thermal-fr properties
Melting temperature ASTM E967-DSC °C - 220 220
Heat deflection temperature, 4.6 ㎏/cm2 (66 psi) ASTM D648 °C - - -
Heat deflection temperature, 18.5 ㎏/cm2 (264 psi) ASTM D648 °C - 185 200
Flammability UL94 - - HB HB
Physical properties
Hardness ASTM D2240 Shore D D Dry / Cond* 77 / 75 78 / 77
Density ASTM D792 g/cm3 - 1.18 1.25
Molding shrinkage normal or perpendicular ASTM D955 % - 1.50 1.10
Test sample conditions, Test sample conditions, Dry= Measurements at 23°C, RH50. Test after molded 1 - 2 hr. Cond*=Test according to ISO 1110 conditions. For reference only.
PA 6 Glass-fiber Reinforced Grade
Introduction
This product is a composite of PA 6 and 15%, 30% or 45% glass-fiber. There are natural and black colors. Natural color granule could be dyed in various colors. Its impact strength, stiffness and heat deflection temperature are better than PA 6. Its machinability and surface appearance are better than PA 66 glass-fiber reinforced grade.
Applications
1. Handle of the hand-tool
2. Accessories of the camera
3. Brake-handle of the bicycle
4. Housing of the electric tool
5. Gear
6. Gasoline filter of the car
7. Legs of the chair
8. Rearview mirror rack of the car
Features
1. Good Stiffness
2. Heat-resistance
3. Good surface appearance
4. Easy to be painted / coated
Mechanical properties Standard Unit Test sample conditions PA 6 Glass-fiber Reinforced Grade
G-4030-G3-NC G-4030-G6-NC G-4030-G9 -NC
Tensile Strength at Yield ASTM D638 Kg/cm2 Dry / Cond* 1200 / 780 1600 / 1100 1900 / 1500
Elongation at Break ASTM D638 % Dry / Cond* 7 / 14 6 / 13 5 / 11
Tensile Strength at Break ASTM D638 Kg/cm2 Dry / Cond* 1200 / 780 1600 / 1100 1900 / 1500
Tensile modulus ASTM D638 Kg/cm2 Dry / Cond* 27000 / 20800 58000 / 23000 69000 / 48900
Flexural strength ASTM D790 Kg/cm2 Dry / Cond* 1950 / 1200 2400 / 1800 3000 / 2400
Flexural modulus ASTM D790 Kg/cm2 Dry / Cond* 38000 / 22800 62000 / 31000 95000 / 61000
Izod notched impact strength ASTM D256 Kg-cm/cm Dry / Cond* 5.5 / 11.5 11.5 / 18 13.5 / 18.5
Thermal-fr properties
Melting temperature ASTM E967-DSC °C - 220 220 220
Heat deflection temperature, 4.6 ㎏/cm2 (66 psi) ASTM D648 °C - - - -
Heat deflection temperature, 18.5 ㎏/cm2 (264 psi) ASTM D648 °C - 200 205 210
Flammability UL94 - - HB HB HB
Physical properties
Hardness ASTM D2240 Shore D D Dry / Cond* 81 / 77 83 / 81 85 / 84
Density ASTM D792 g/cm3 - 1.23 1.37 1.51
Molding shrinkage normal or perpendicular ASTM D955 % - 1.68 1.14
Test sample conditions, Test sample conditions, Dry= Measurements at 23°C, RH50. Test after molded 1 - 2 hr. Cond*=Test according to ISO 1110 conditions. For reference only.
PA 6 Glass- / Mineral-fiber Reinforced Grade.
Introduction
This product is a composite of PA 6 and 20%, 35% or 45% glass- and mineral-fiber. Its strength, stiffness and heat deflection temperature are better than PA 6. Its dimensional stability, longitudinal / transverse shrinkage and surface appearance are better than PA 66 glass-fiber reinforced grade.
Applications
1. Handles of the hand-tool
2. Housing of the headlight reflection
3. Handle of the spray gun
4. Accessories of the car
5. Components of the engine
Features
1. Good surface appearance
2. Excellent knock resistance
3. Good dimensional stability
4. Easy to be painted
5. Good electroplating performance
Mechanical properties Standard Unit Test sample conditions PA 6 Glass- / Mineral-fiber Reinforced Grade.
GM-4030 GM-4035 GM-1040
Tensile Strength at Yield ASTM D638 Kg/cm2 Dry / Cond* 1120 / 660 1150 / 680 1300 / 850
Elongation at Break ASTM D638 % Dry / Cond* 2.5 / 9 2.5 / 7.5 2.5 / 6
Tensile Strength at Break ASTM D638 Kg/cm2 Dry / Cond* 850 / 470 990 / 520 1050 / 630
Tensile modulus ASTM D638 Kg/cm2 Dry / Cond* 43000 / 24500 43500 / 25000 51500 / 32800
Flexural strength ASTM D790 Kg/cm2 Dry / Cond* 1650 / 1050 1800 / 1080 2040 / 1300
Flexural modulus ASTM D790 Kg/cm2 Dry / Cond* 58000 / 31500 71100 / 32500 76100 / 42300
ASTM D256 Kg-cm/cm Dry / Cond* 5.0 / 8.5 5.5 / 9.5 8.0 / 11.5
Thermal-fr properties
Melting temperature ASTM E967-DSC °C - 220 220 220
Heat deflection temperature, 4.6 ㎏/cm2 (66 psi) ASTM D648 °C - - - -
Heat deflection temperature, 18.5 ㎏/cm2 (264 psi) ASTM D648 °C - 200 200 200
Flammability UL94 - - HB HB HB
Physical properties
Hardness ASTM D2240 Shore D D Dry / Cond* 80 / 74 80 / 73 83 / 76
Density ASTM D792 g/cm3 - 1.37 1.43 1.49
Molding shrinkage normal or perpendicular ASTM D955 % - 0.34 0.28 0.21
Test sample conditions, Test sample conditions, Dry= Measurements at 23°C, RH50. Test after molded 1 - 2 hr. Cond*=Test according to ISO 1110 conditions. For reference only.